| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM1609 Acetal, Molybdenum Disulfide Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Molybdenum disulfide filled polyacetal for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | DIN 53479 |
| Water Absorption | 0.22 % | 0.22 % | DIN 53495 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 82 | 82 | ASTM-D785 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
| Elongation at Break | 40 % | 40 % | ASTM-D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM-D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | DIN 53461 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Network Polymers NPP 50-0548
- Phillips 66 COPYLENE® CR750CL-02 Polypropylene, Random Copolymer, NX-8000 based
- MarkeTech Repton 115 Aluminum Oxide
- Lubriplate SYNCOOL 46 Polyglycolester-Based Synthetic Air Compressor Fluid
- Teknor Apex APEX® 90-A472R-65-NT Polyvinyl Chloride, Flexible
- Tipco Tipcolene® FPT 10 - 10% Talc Reinforced Polypropylene Homopolymer
- Asia International Enterprise (Hong Kong) 60G4 Nylon 66, 20% Filled
- Axiall 6651 Moldings & Extrusions Flexible PVC
- LTL Color Compounds ColorFast® FRPS200 Styrene, High Impact
Copyright © lookpolymers.com All Rights Reserved