Aremco Aremco-Bond™ 568 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 568 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aluminum-Filled, 1:1, Good Bond Strength and High Thermal Conductivity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.850 g/cc | 0.850 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | |
| Flexural Strength | 78.6 MPa | 11400 psi | ASTM D790 |
| Shear Strength | 17.2 MPa | 2500 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 59.4 µm/m-°C @Temperature 20.0 °C |
33.0 µin/in-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 1.30 W/m-K | 9.00 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |
| Shrinkage | 0.20 % | 0.20 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | |
| Dielectric Strength | 3.15 kV/mm | 80.0 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Recommended Cure |
| 1440 - 2880 min @Temperature 23.0 °C |
24.0 - 48.0 hour @Temperature 73.4 °F |
Alternate Cure | |
| Pot Life | 240 min @Temperature 25.0 °C |
240 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Excellent | |
| Color | Gray | |
| Mix Ratio By Weight | 1:1 | resin:hardener |
| Mixed Viscosity | Paste |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD: 20-30 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Materion Beryllium Nickel Strip - Alloy 360 MH10, Mill Hardened
- Lucas-Milhaupt Silvaloy® 50N Brazing Alloy
- Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/32 Polyurethane Casting Elastomer
- Teknor Apex Monprene® MP-1564L3 Thermoplastic Elastomer
- A. Schulman POLYBLAK™ 3422 Black Color Concentrate, 35% Carbon Black Based In LDPE
- Hexcel® HexForce™ 1522 Fiber Glass Fabric
- A. Schulman ComAlloy Hiloy® 414 Polyester - PBT, Glass Reinforced
- Ashley Polymers Ashlene® D925LH-30G Nylon 12, 30% Glass Reinforced, Lubricated
Copyright © lookpolymers.com All Rights Reserved