Cosmic Plastics 224 Dacron Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Molded, Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics 224 Dacron Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | |
| Apparent Bulk Density | 0.270 g/cc | 0.00975 lb/in³ | |
| Water Absorption | 0.35 % | 0.35 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 25.0 - 36.0 MPa | 3630 - 5220 psi | |
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Compressive Strength | 141 MPa | 20500 psi | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Heat Distortion temperature |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
Wet |
| 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.0080 @Frequency 1000 Hz |
0.0080 @Frequency 1000 Hz |
Wet |
| 0.012 @Frequency 1e+6 Hz |
0.012 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 125 sec | 125 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Quadrant EPP Ertacetal® H-TF POM-H, PTFE-filled, extruded (ISO Data)
- Quadrant EPP Ertalyte® PET-P, Polyester-semi-crystalline thermoplastic, extruded (ASTM Product Data Sheet)
- SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer (Europe-Africa-Middle East)
- Chevron Phillips HiD® 9354 HDPE Natural Pipe Resin (discontinued **)
- Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact
- A. Schulman POLYBLAK™ 4642 Premium Black Color Concentrate, 40% Carbon Black Based In LLDPE
- Cytec Thornel® T-300 3K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- 3M FM1542 Clear Polyester Label Products
- 3M FM02511K Clear Laser Imprintable Label Product
- Beijing Ranger Chem SM-828X80 Solvent Based Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved