Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Multibase
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Multibase

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/inÂ³	Relative, molded-without post cure; ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	31	31	molded- without post cure; ASTM D2240
	37	37	post cured- 2 hours at 177Â°C; ASTM D2240
	37	37	post cured- 4 hours at 177Â°C; ASTM D2240
	38	38	post cured- 8 hours at 177Â°C; ASTM D2240
Tensile Strength, Ultimate	6.89 MPa	1000 psi	molded-without post cure; ASTM D412
	7.58 MPa	1100 psi	post cured- 2 hours at 177Â°C; ASTM D412
	7.58 MPa	1100 psi	post cured- 8 hours at 177Â°C; ASTM D412
	8.96 MPa	1300 psi	post cured- 4 hours at 177Â°C; ASTM D412
Tensile Strength, Yield	0.965 MPa	140 psi	at 200%, molded-without post cure; ASTM D412
	1.24 MPa	180 psi	at 200%, post cured- 2 hours at 177Â°C; ASTM D412
	1.31 MPa	190 psi	200%, post cured- 4 hours at 177Â°C; ASTM D412
	1.31 MPa	190 psi	200%, post cured- 8 hours at 177Â°C; ASTM D412
Elongation at Break	760 %	760 %	post cured- 8 hours at 177Â°C; ASTM D412
	810 %	810 %	molded-without post cure; ASTM D412
	810 %	810 %	post cured- 2 hours at 177Â°C; ASTM D412
	810 %	810 %	post cured- 4 hours at 177Â°C; ASTM D412
Tear Strength	19.3 kN/m	110 pli	Die B,molded-without post cure; ASTM D624
	21.0 kN/m	120 pli	Die B,post cured- 2 hours at 177Â°C; ASTM D624
	21.0 kN/m	120 pli	Die B, post cured- 4 hours at 177Â°C; ASTM D624
	24.5 kN/m	140 pli	Die B, post cured- 8 hours at 177Â°C; ASTM D624
Compression Set	66 %	66 %	22 hours at 177Â°C, post cured- 8 hours at 177Â°C; ASTM D395
	78 %	78 %	22 hours at 177Â°C, post cured- 4 hours at 177Â°C; ASTM D395
	82 %	82 %	22 hours at 177Â°C, post cured- 2 hours at 177Â°C; ASTM D395
	90 %	90 %	22 hours at 177Â°C, molded-without post cure; ASTM D395

Thermal Properties	Metric	English	Comments
Shrinkage	2.10 % @Temperature 177 Â°C, Time 14400 sec	2.10 % @Temperature 351 Â°F, Time 4.00 hour	post cured
	2.20 % @Temperature 177 Â°C, Time 7200 sec	2.20 % @Temperature 351 Â°F, Time 2.00 hour	post cured
	2.50 % @Temperature 177 Â°C, Time 28800 sec	2.50 % @Temperature 351 Â°F, Time 8.00 hour	post cured

Users viewing this material also viewed the following: