Clariant Renol PBTG30-L Polybutylene Terephthalate, 30% Glass Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PBTG30-L Polybutylene Terephthalate, 30% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D648 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Temperature 22.8 °C |
1.20 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 113 °C |
2 - 4 hour @Temperature 235 °F |
to ensure moisture content is less than 0.05% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 CF 40 PA66, 40% carbon fibre
- Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced
- ICO Polymers ICORENEâ„¢ 115-1325 LMDPE Rotational Molding Resin
- Lord Adhesives 513 Fast Cure, Non-Sagging Acrylic Adhesive
- LG Chemical 82TR SAN, High Transparency, Heat Resistance, Chemical Resistance
- Total 2287 HDPE Bimodal Film Resin
- Goodfellow Nickel 81/Iron 19 Alloy
- Fainplast Compounds CKL 0411/UV Flexible PVC, Sheathing Lead Free
- Arkema Group OREVAC® 18360 Maleic Anhydride Modified Polyethylene
- Solvay Specialty Polymers Amodel® DW-1150 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved