Solvay Specialty Polymers Solef® 21510 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 21510 Polyvinylidene Fluoride (PVDF)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 21510 PVDF copolymer has low viscosity and is suitable for solution processing in lithium batteries applications.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 |
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec |
<= 0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Melt Flow | 3.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
3.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2900 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 15.0 - 18.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2180 - 2610 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Break | 600 - 750 % @Thickness 2.00 mm, Temperature 23.0 °C |
600 - 750 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Yield | 12 - 15 % @Thickness 2.00 mm, Temperature 23.0 °C |
12 - 15 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.360 - 0.480 GPa @Thickness 2.00 mm, Temperature 23.0 °C |
52.2 - 69.6 ksi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 20.0 - 24.0 J/g | 8.60 - 10.3 BTU/lb | Crystallization Heat; ASTM D3417 |
| 20.0 - 24.0 J/g | 8.60 - 10.3 BTU/lb | ASTM D3417 | |
| Melting Point | 130 - 136 °C | 266 - 277 °F | ASTM D3418 |
| Crystallization Temperature | 89.0 - 93.0 °C | 192 - 199 °F | Peak, DSC; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Copolymer | |
| Low Viscosity | ||
| Generic | PVDF | |
| Processing Method | Solution Processing | |
| Uses | Batteries |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified)
- Flint Hills P6G2Z-090 Impact Copolymer Polypropylene
- Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)
- Techmer ES Plaslube® J-1/CF/10/TF/13/SI/2 BK223 PA66
- Ensinger Tecapeek® XP-90 Compression Molded PEEK Compound, 25% Fiberglass
- Domo 2340P Polypropylene Copolymer
- Ineos ABS Centrex® 825 ASA+AES Blend (discontinued **)
- Karina 38/49-FC-LMP Straw Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved