Clariant Renol BR7039G15 Nylon 6, 15% Glass Fiber, bondable to TPU
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol BR7039G15 Nylon 6, 15% Glass Fiber, bondable to TPU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Filler Content | 15 % | 15 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.001 MPa | 10878 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 125.0 MPa | 18130 psi | ASTM D790 |
| Flexural Modulus | 4.43 GPa | 643 ksi | ASTM D790 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.827 MPa | 50.0 - 120 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP COLORCOMP J1000Z PES (Europe-Africa-Middle East)
- LG Chemical LK170 PVC
- Karina 752-12/6-Y-BZ Ruby Red PVC Compound
- Zhejiang Juner JEPP2056 PP For Automotive Parts
- Zylog Hipolyene® 8021 M Thermoplastic Polyolefin & PP Compound
- Epoxyset Epoxiohm EO-30M-1 Electrically Conductive Epoxy Adhesive
- BASF Novolen® 2500 H Polypropylene
- 3M 5360K Silicone Rubber Termination Kits
- EMS-Grivory Grivory® GV-6H EF nat PA*-GF60
- Guarniflon PTFE G300 Polytetrafluoroethylene
Copyright © lookpolymers.com All Rights Reserved