Clariant PA213N40 Nylon 6, Mineral/Glass Reinforced, Heat Stabilized, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced , Nylon 6, Heat Stabilized |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant PA213N40 Nylon 6, Mineral/Glass Reinforced, Heat Stabilized, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Filler Content | 40 % | 40 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 141 MPa | 20500 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C |
0.900 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 282 °C | 480 - 540 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- MV Labs NI450 {Ni(NH3)6}Cl2 Hexaminenickel(II) chloride
- PolyOne Dynaflex™ G7970-9001-02 Thermoplastic Elastomer (TPE)
- Chevron Phillips Ryton® R-7 Polyphenylene Sulfide Compound (discontinued **)
- Engineered Syntactic Systems SF-22 Subsea Macrosphere Syntactic Void Filler
- DSM Arnitel® PM581 58 Shore D, Extrusion Grade Copolyester Elastomer (North America)
- Daikin NEOFLON AC-5600 PFA Coating Powder, White
- Dow Corning 360 Medical Fluid, 1000 CST.
- Bapolan® PS6078-G Polystyrene Compound
- Ashley Polymers Ashlene® L927 Nylon 12
- Technetics Group PLASTOLON™ Unsintered PTFE tape (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved