- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Chi Mei Polylac® PA-777B ABS - High Heat
Chi Mei Polylac® PA-777B ABS - High Heat
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-777B ABS - High Heat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Heat Impact
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.7 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.7 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Ball Indentation Hardness | 91.0 MPa | 13200 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 18 % | 18 % | 50 mm/min; ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 2.05 J/cm @Thickness 6.35 mm |
3.84 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.38 J/cm @Thickness 3.17 mm |
4.46 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Impact | 14.0 | 14.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | unannealed; ISO 75 |
| 105 °C | 221 °F | annealed; ISO 75 | |
| Vicat Softening Point | 105 °C @Load 5.00 kg |
221 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 107 °C @Load 5.00 kg |
225 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 113 °C @Load 1.00 kg |
235 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 115 °C @Load 1.00 kg |
239 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Plasma Coatings 15000 Surface Material
- SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched
- Taiwan Sheen Soon Sheenthane® AS-626H TPU for PU Adhesive
- Silberline Silvet® 220-30-E1
- Topas Advanced Polymers TOPAS® 6013M-07 Cyclic Olefin Copolymer (COC)
- A. Schulman INVISION™ VX-5085UI Soft Touch Polyolefin Thermoplastic
- Tra-Con Tra-Bond 724-17GR Polyurethane Adhesive
- Trelleborg Emerson & Cuming Eccobond® TP 50 Two-Component Low Temperature Performance Silicone Adhesive
- Zoltek Pyron® Scrim Oxidized Pan Fiber
- Eurostar Staramide RF006SXS PA66, 30% Glass Fiber Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved