Lanxess Durethan® AKV 325 H2.0 901510 Nylon 66, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 325 H2.0 901510 Nylon 66, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 25% glass fibers, extrusion- and blow molding grade, branched, high viscosity, good heat-ageing resistance, good hydrolysis resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Viscosity Test | 210 cm³/g | 210 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Melt Flow | 9 g/10 min @Load 5.00 kg, Temperature 290 °C |
9 g/10 min @Load 11.0 lb, Temperature 554 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 160 MPa | 23200 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 |
| 10 % | 10 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.30 GPa | 769 ksi | Conditioned; ISO 527-1/-2 |
| 8.80 GPa | 1280 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 862 | 862 | Puncture maximum force (N); ISO 6603-2 |
| 747 @Temperature -30.0 °C |
747 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.60 J | 1.92 ft-lb | ISO 6603-2 |
| 2.10 J @Temperature -30.0 °C |
1.55 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.10 J @Temperature -30.0 °C |
1.55 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Vicat Softening Point | 250 °C | 482 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,EH,22-090,GF25 | |
| Processing | Blow molding | |
| Profile extrusion | ||
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-50 Supported Urethane Foam, Firm, PET Supported
- Polykemi AB SCANBLEND P AP2060 F30 PBT/ASA, Glass Fiber Reinforced
- SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Europe-Africa-Middle East)
- Lavergne VYSTYRENE PS 3904 High Impact Polystyrene
- Covestro Bayblend® T 64 Polycarbonate/ABS Blend
- 3M FM159G Clear Polyester Overlaminate Label Products
- ACC MM239 Addition Cure 2-Part Molding Rubber
- ChevronTexaco ISO 22 Form Oil
- Sumitomo Bakelite North America FM 4017F Fiberglass and Mineral Reinforced Phenolic
Copyright © lookpolymers.com All Rights Reserved