- Chi Mei Polylac® PA-764B ABS - Flame Retardant
Chi Mei Polylac® PA-764B ABS - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-764B ABS - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
F.R. Weather Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 78.0 MPa | 11300 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179 |
| Impact | 11.0 | 11.0 | Impact Flexural Test Notched (KJ/m²) |
| 110 | 110 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | unannealed; ISO 75 |
| 97.0 °C | 207 °F | annealed; ISO 75 | |
| Vicat Softening Point | 85.0 °C @Load 5.00 kg |
185 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 88.0 °C @Load 5.00 kg |
190 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 99.0 °C @Load 1.00 kg |
210 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 99.0 °C @Load 1.00 kg |
210 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 2.54 mm |
V-0 @Thickness 0.100 in |
UL 94 |
| 5VA @Thickness 3.17 mm |
5VA @Thickness 0.125 in |
UL 94 |
Users viewing this material also viewed the following:
- MV Labs ND900 NdPO4·xH2O Neodymium phosphate hydrate
- Sumitomo Chemical ESPOLEX® 820 Thermoplastic Elastomer
- Lubrizol ESTANE® T5090 Ether Based Thermoplastic Polyurethane (European Grade)
- Westlake EF524 14.5% Ethylene Vinyl Acetate Copolymer
- Total PPC 4944WZ Polypropylene, Impact Copolymer
- CLAL-MSX NICLAFOR® 1000 TH3 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy
- Ashley Polymers Ashlene® 830L-30G Nylon 6, 30% Glass Reinforced
- A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer
- PolyOne Lubri-Tech™ AT-000/02T Acetal - 2% PTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved