SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. UL94 V0 and 5VA listed.
Physical Properties Metric English Comments
Specific Gravity 1.51 g/cc
1.51 g/cc
ASTM D792
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.90 %
0.90 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.6 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 7.6 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 158 MPa
22900 psi
Type I, 5 mm/min; ASTM D638
165 MPa
23900 psi
5 mm/min; ISO 527
Tensile Strength, Yield 165 MPa
23900 psi
5 mm/min; ISO 527
168 MPa
24400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 9.23 GPa
1340 ksi
5 mm/min; ASTM D638
9.50 GPa
1380 ksi
1 mm/min; ISO 527
Flexural Yield Strength 220 MPa
31900 psi
1.3 mm/min, 50 mm span; ASTM D790
225 MPa
32600 psi
2 mm/min; ISO 178
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
9.25 GPa
1340 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
0.900 J/cm

@Temperature -30.0 °C
 1.69 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.0 µm/m-°C

@Temperature -20.0 - 150 °C
 8.89 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
16.0 µm/m-°C

@Temperature 23.0 - 150 °C
 8.89 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 41.0 µm/m-°C

@Temperature -20.0 - 150 °C
 22.8 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
41.0 µm/m-°C

@Temperature 23.0 - 150 °C
 22.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
208 °C

@Thickness 3.20 mm
 406 °F

@Thickness 0.126 in
 unannealed; ASTM D648
210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 213 °C
415 °F
Rate B/50; ISO 306
220 °C
428 °F
Rate B/120; ISO 306
228 °C
442 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F