- Hexcel® HexPly® 954-3 Curing Cyanate Resin, M55J Fiber
Hexcel® HexPly® 954-3 Curing Cyanate Resin, M55J Fiber
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® 954-3 Curing Cyanate Resin, M55J Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa @Temperature 23.0 °C |
5080 psi @Temperature 73.4 °F |
90° |
| 2303 MPa @Temperature 23.0 °C |
334000 psi @Temperature 73.4 °F |
0° | |
| Tensile Modulus | 6.20 GPa @Temperature 23.0 °C |
899 ksi @Temperature 73.4 °F |
90° |
| 324 GPa @Temperature 23.0 °C |
47000 ksi @Temperature 73.4 °F |
0° | |
| Compressive Yield Strength | 951 MPa @Temperature 23.0 °C |
138000 psi @Temperature 73.4 °F |
|
| Compressive Modulus | 306 GPa @Temperature 23.0 °C |
44400 ksi @Temperature 73.4 °F |
|
| Shear Strength | 80.0 MPa @Temperature 22.0 °C |
11600 psi @Temperature 71.6 °F |
0° |
Users viewing this material also viewed the following:
- PolyOne Synplast™ TOTM-N Tri (2-ethylhexyl) Trimellitate
- Pinnacle Polymers 3208 High Impact Polypropylene Copolymer, Injection Molding Grade
- ITW Plexus Plexusâ„¢ MA820 Methacrylate Adhesive
- LATI Latistat 36/MR-04 ABS
- SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66 (Asia Pacific)
- ChevronTexaco Cepheus® 220
- Ametek 17-4 P/M Process, Sintered at 2050°F (1121°C)
- A. Schulman POLYBATCH™ White 8000 AP Concentrate Based In LDPE
Copyright © lookpolymers.com All Rights Reserved