PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Heat Treatment Condition T6 (Quench in water at RT)abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.4605 - 2.7195 g/cc
0.088891 - 0.098248 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 160
>= 160
Tensile Strength at Break >= 348 MPa

@Temperature 150 °C
 >= 50500 psi

@Temperature 302 °F
>= 380 MPa

@Temperature 20.0 °C
 >= 55100 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 310 MPa

@Temperature 150 °C
 >= 45000 psi

@Temperature 302 °F
>= 350 MPa

@Temperature 20.0 °C
 >= 50800 psi

@Temperature 68.0 °F
Elongation at Break >= 0.40 %

@Temperature 20.0 °C
 >= 0.40 %

@Temperature 68.0 °F
>= 0.70 %

@Temperature 150 °C
 >= 0.70 %

@Temperature 302 °F
Modulus of Elasticity >= 81.0 GPa

@Temperature 150 °C
 >= 11700 ksi

@Temperature 302 °F
>= 88.0 GPa

@Temperature 20.0 °C
 >= 12800 ksi

@Temperature 68.0 °F
Poissons Ratio 0.297

@Temperature 20.0 °C
 0.297

@Temperature 68.0 °F
0.297

@Temperature 100 °C
 0.297

@Temperature 212 °F
0.299

@Temperature 150 °C
 0.299

@Temperature 302 °F
0.302

@Temperature 200 °C
 0.302

@Temperature 392 °F
0.302

@Temperature 250 °C
 0.302

@Temperature 482 °F
0.305

@Temperature 300 °C
 0.305

@Temperature 572 °F
Shear Modulus 32.0 GPa

@Temperature 300 °C
 4640 ksi

@Temperature 572 °F
33.0 GPa

@Temperature 250 °C
 4790 ksi

@Temperature 482 °F
34.0 GPa

@Temperature 150 °C
 4930 ksi

@Temperature 302 °F
34.0 GPa

@Temperature 200 °C
 4930 ksi

@Temperature 392 °F
35.0 GPa

@Temperature 100 °C
 5080 ksi

@Temperature 212 °F
36.0 GPa

@Temperature 20.0 °C
 5220 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 15.4 - 16.4 µm/m-°C

@Temperature 20.0 - 100 °C
 8.56 - 9.11 µin/in-°F

@Temperature 68.0 - 212 °F
15.6 - 16.6 µm/m-°C

@Temperature 20.0 - 200 °C
 8.67 - 9.22 µin/in-°F

@Temperature 68.0 - 392 °F
16.3 - 17.3 µm/m-°C

@Temperature 20.0 - 300 °C
 9.06 - 9.61 µin/in-°F

@Temperature 68.0 - 572 °F
Specific Heat Capacity 0.860 - 0.900 J/g-°C
0.206 - 0.215 BTU/lb-°F
Thermal Conductivity 118.9 W/m-K

@Temperature 400 °C
 825.2 BTU-in/hr-ft²-°F

@Temperature 752 °F
123.6 W/m-K

@Temperature 200 °C
 857.8 BTU-in/hr-ft²-°F

@Temperature 392 °F
123.8 W/m-K

@Temperature 300 °C
 859.2 BTU-in/hr-ft²-°F

@Temperature 572 °F
126.5 W/m-K

@Temperature 100 °C
 877.9 BTU-in/hr-ft²-°F

@Temperature 212 °F
131.6 W/m-K

@Temperature 30.0 °C
 913.3 BTU-in/hr-ft²-°F

@Temperature 86.0 °F
Melting Point 537 - 833 °C
999 - 1530 °F
Solidus 537.1 - 543.1 °C
998.8 - 1010 °F
Liquidus 826.5 - 832.5 °C
1520 - 1531 °F
Component Elements Properties Metric English Comments
Aluminum, Al 68 %
68 %
As Balance
Copper, Cu 1.0 %
1.0 %
Magnesium, Mg 1.0 %
1.0 %
Silicon, Si 30 %
30 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000660 - 0.00000700 ohm-cm
0.00000660 - 0.00000700 ohm-cm