CENTROPLAST CENTROMID 6 E FG Polyamide 6 extruded, Food Grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | CENTROPLAST Engineering Plastics GMBH |
| Trade Name | CENTROMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CENTROPLAST CENTROMID 6 E FG Polyamide 6 extruded, Food Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This tough and impact resistant material has good chemical resistance and can be bonded and welded. Information provided by CENTROPLAST Engineering Plastics GMBH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 9.0 % | 9.0 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 @Thickness 10.0 mm |
85 @Thickness 0.394 in |
ISO 2039-2 |
| Ball Indentation Hardness | 150 MPa | 21800 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | v = 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2 |
| Tensile Modulus | 3.25 GPa | 471 ksi | ISO 527-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | |
| Melting Point | 220 °C | 428 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | Long Term |
| 160 °C | 320 °F | Short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| HB @Thickness 6.00 mm |
HB @Thickness 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | in transformer oil; IEC 60243-1 |
| Dissipation Factor | 0.019 @Frequency 100 Hz |
0.019 @Frequency 100 Hz |
IEC 60250 |
| 0.021 @Frequency 1e+6 Hz |
0.021 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Food Compliance | Yes | BfR |
| Yes | FDA |
Users viewing this material also viewed the following:
- MV Labs ZR550 (NH4)2ZrF6 Ammonium hexafluorozirconate (Hf< 50 ppm)
- Cookson Group Plaskon® S-7P Epoxy Encapsulant (discontinued **)
- Solvay Chemicals Free Flowing Barium Hydroxide Octahydrate
- Sumitomo Bakelite North America RX® 3-1-501N-P Mineral Filled Diallyl Phthalate
- Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, Conditioned
- Chevron Phillips MarFlex® 5440 Low Density Polyethylene, Cast Film
- ChevronTexaco 100 Aviation Gasoline
- Radici Radilon® S 38F (dry) Nylon 6
Copyright © lookpolymers.com All Rights Reserved