Barlog Plastics KEBATER BM330 PBT, 30% mineral reinforced, good light reflection
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATER |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATER BM330 PBT, 30% mineral reinforced, good light reflection.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT-MD30Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | similar to ISO 62 test |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527-1 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527-1 |
| Charpy Impact Unnotched | NB | NB | ISO 179-1eU |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PBT-MD30 |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 3 Rod and Bar; AT (TF00) Temper; All Sizes (UNS C17510)
- Karina E 75800-35/1-B-AC Ivory PVC Compound
- Saint-Gobain CHR® H7575 Glass-Silicone Backing Silicone Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics LNP THERMOCOMP DC006 PC (Asia Pacific)
- Sibur SKS-30 ARKPN 3rd Group Styrene-Butadiene Rubber (SBR)
- A. Schulman LP481 Molding Grade High-Density Polyethylene
- Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled
- Cytec Thornel® Mat VMC Carbon Fiber
- Chi Mei Wonderloy® PC-385 PC/ABS Alloy
Copyright © lookpolymers.com All Rights Reserved