DuPont™ Kapton® 200ZT Polyimide Film, 50 Micron Thickness

Category Polymer , Film , Thermoset , Polyimide, TS , Polyimide, Thermoset Film
Manufacturer DuPont
Trade Name Kapton®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Kapton® 200ZT Polyimide Film, 50 Micron Thickness.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film thickness 50 micron 2.0 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Similar to Kapton® Type VN and HN with superior bondability. Available in thicknesses from 0.3 mil (7.5 µm) to 5 mil (125 µm).General Kapton® information: Kapton® is synthesized by polymerizing an aromatic dianhydride with an aromatic diamine. It has excellent chemical resistance; there are no known organic solvents for the film. It does not melt. It can be used at both high and low temperature extremes. Kapton® polyimide films can be used in a variety of electrical and electronic uses: wire and cable tapes, formed coil insulation, substrates for printed circuit boards, motor slot liners, magnet wire insulation, transformer and capacitor insulation, magnetic and pressure-sensitive tapes, and tubing.Data provided by DuPont High Performance Films.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Water Absorption 2.8 %
2.8 %
24 hr/23°C. ASTM D570
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 75 %
75 %
Orientation not specified; ASTM D882
Poissons Ratio 0.34
0.34
Value for Kapton® HN
Secant Modulus 2.80 GPa
406 ksi
ASTM D882
Coefficient of Friction, Dynamic 0.48
0.48
Value for Kapton® HN. Film to film. ASTM D1894-90
Coefficient of Friction, Static 0.63
0.63
Value for Kapton® HN. Film to film. ASTM D1894-90
Film Tensile Strength at Break, MD 221 MPa
32100 psi
Orientation not specified; ASTM D882
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature 20.0 °C
11.1 µin/in-°F

@Temperature 68.0 °F
Value for Kapton® HN
32.0 µm/m-°C

@Temperature 100 °C
17.8 µin/in-°F

@Temperature 212 °F
Value for Kapton® HN
40.0 µm/m-°C

@Temperature 250 °C
22.2 µin/in-°F

@Temperature 482 °F
Value for Kapton® HN
Specific Heat Capacity 1.09 J/g-°C
0.261 BTU/lb-°F
Value for Kapton® HN
Thermal Conductivity 0.120 W/m-K
0.833 BTU-in/hr-ft²-°F
Value for Kapton® HN
Maximum Service Temperature, Air 400 °C
752 °F
Kapton® can function after brief exposure to 400°C (750°F). Various grades are UL rated for continuous service at 220-240°C (430-460°F).
Minimum Service Temperature, Air -269 °C
-452 °F
Maintains properties and flexibility
Glass Transition Temp, Tg 385 °C
725 °F
Value for Kapton® HN
Flammability, UL94 V-0
V-0
Optical Properties Metric English Comments
Refractive Index 1.70

@Wavelength 589.3 nm
1.70

@Wavelength 589.3 nm
Value for Kapton® HN.  Na D line; ASTM D542-90
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
Kapton® HN in damp heat; IPC-TM-650; Method 2.5.17
1.00e+17 ohm-cm
1.00e+17 ohm-cm
per ASTM D257-91 for Kapton® HN
Dielectric Constant 3.6

@Frequency 1000 Hz
3.6

@Frequency 1000 Hz
Use evaporated metal electrodes, two terminal system of measurement at standard conditions.; ASTM D150
Dielectric Strength 217 kV/mm
5510 kV/in
Flat sheets in air placed between 1/4 in diameter brass electrodes with 0.8 mm (1/32 in) edge radius subjected to 60 cycles AC voltage at 600V/s rate of rise to the breakdown voltage.; ASTM D149-81
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
Same test as dielectric constant.