BASF Ultramid® Seal-Fit PA6/66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® Seal-Fit PA6/66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Transparent, tough, amorphous copolyamide for injection molding, specially developed for tight overmoulding of metal inlays.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 4.5 - 5.0 % | 4.5 - 5.0 % | ISO 62 |
| Viscosity Measurement | 125 | 125 | ISO 307 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 |
| Melt Flow | 82.5 g/10 min @Load 10.0 kg, Temperature 230 °C |
82.5 g/10 min @Load 22.0 lb, Temperature 446 °F |
ISO 1133 |
| 132 g/10 min @Load 5.00 kg, Temperature 275 °C |
132 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | ISO 868 |
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-1/-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 - 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 - 66.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 - 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 - 66.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 °C | 135 °F | ISO 75-1/-2 |
| Vicat Softening Point | 68.0 °C @Load 5.10 kg |
154 °F @Load 11.2 lb |
ISO 306 |
| Decomposition Temperature | >= 300 °C | >= 572 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 30.0 °C | 86.0 °F | Hopper Throat |
| Zone 1 | 200 °C | 392 °F | Feed Zone |
| Zone 2 | 240 °C | 464 °F | Compression |
| Zone 3 | 240 °C | 464 °F | Metering-zone |
| Zone 4 | 240 °C | 464 °F | Nozzle |
| Melt Temperature | 240 °C | 464 °F | Optimal |
| 230 - 260 °C | 446 - 500 °F | Injection-molding/Extrusion | |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Injection-molding |
| 40.0 °C | 104 °F | Optimal | |
| Drying Temperature | 60.0 °C | 140 °F | |
| Dry Time | 8 hour | 8 hour | |
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal |
| <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | >400°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |
Users viewing this material also viewed the following:
- BASF Master Builders Solutions ChemRex® CX-26 Isocyanate-Free Polyurethane-Based Sealant (discontinued **)<
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 93A
- Unitika elitel UE3200 Polyester, Pellet
- A. Schulman POLYBATCH™ Green 3373 Concentrate Based In Polyethylene
- Cytec Thornel® P-120S 2K Carbon Fiber, Pitch Precursor
- China-Yixing Longly Refractories Zirconia Ceramics
- 3M Bumpon™ SJ5816 Resilient Rollstock
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N339 Filler
- Beijing Chemical Industry KAIFA® MN301-G20 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved