CeramTec V 679 Alumina, 99.7%
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CeramTec North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CeramTec V 679 Alumina, 99.7%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.90 g/cc | 0.141 lb/in³ | DIN EN 623-2 |
| Water Absorption | 0.00 % | 0.00 % | Open Porosity; DIN EN 623-2 |
| Permeability | 0.00 | 0.00 | %, Gas |
| Weibull Modulus | 10 | 10 | DINV ENV 843-5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 1750 | 1750 | HV1; DINV ENV 843-4 |
| Tensile Modulus | 390 GPa | 56600 ksi | Young's; DINV ENV 843-2 |
| Flexural Strength | 300 MPa | 43500 psi | DIN EN 843-1 |
| Compressive Strength | 2500 MPa | 363000 psi | DIN 51067T1 |
| Poissons Ratio | 0.23 | 0.23 | DINV ENV 843-2 |
| Fracture Toughness | 5.40 MPa-m½ | 4.91 ksi-in½ | K<sub>IC</sub> (SEVNB); DIN CEN/TS 14425-1 |
| Shear Modulus | 159 GPa | 23100 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.50 µm/m-°C @Temperature 20.0 - 400 °C |
4.17 µin/in-°F @Temperature 68.0 - 752 °F |
DIN EN 821-1 |
| 8.50 µm/m-°C @Temperature 20.0 - 1000 °C |
4.72 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN EN 821-1 | |
| Specific Heat Capacity | 0.900 J/g-°C | 0.215 BTU/lb-°F | DINV ENV 821-3 |
| Thermal Conductivity | 30.0 W/m-K | 208 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| Maximum Service Temperature, Air | 1500 °C | 2730 °F | |
| Maximum Service Temperature, Inert | 1500 °C | 2730 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 99.7 % | 99.7 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm @Temperature 400 °C |
1.00e+13 ohm-cm @Temperature 752 °F |
IEC 672-1 |
| 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 | |
| Dielectric Constant | 9.0 @Frequency 1.00e+6 Hz |
9.0 @Frequency 1.00e+6 Hz |
IEC 672-1 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 672-1 |
| Dielectric Loss Index | 0.0010 @Frequency 9.00e+9 Hz |
0.0010 @Frequency 9.00e+9 Hz |
IEC 672-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ra = Arithmetic Mean Roughness Value (µm) | <0.1 | |
| Thermal Shock Resistance R1 (K) | 79 | calculated; R1 = [s? (1-µ)] / (a·E) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Geloy XTWE280 ASA
- Skamol Group Moler 10 Aggregate Insulation
- Supreme Petrochem SC 202LV General Purpose Polystyrene
- Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin
- Assab Steels 705M Machinery Steel
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A
- Aclo Accucomp ABS ABS803L Medium Impact Grade
- Premix Thermoplastics PRE-ELEC® PA 1409 Conductive Thermoplastic Compound
- Axiall 38831 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved