BASF Ultramid® NBX-0025 NF2001 PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® NBX-0025 NF2001 PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | dry; ISO 1183 |
| Water Absorption | 8.5 % | 8.5 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50mm/min; ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 |
| Elongation at Yield | 25 % | 25 % | 50mm/min; ISO 527 |
| Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 5587 Carboxylated Styrene - Butadiene Copolymer
- Plaskolite Optix® PL-150 Acrylic Resin (discontinued **)
- Huntsman IROGRAN® PS455-203 TPU-Polyester
- Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber
- SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Asia Pacific)
- Sumitomo Bakelite North America Epiall® 1908-1 Short Glass Fiber Reinforced Epoxy
- DuPont Performance Polymers Zytel® FN727 BK230A Nylon 6
- California Fine Wire Dumet Nickel Iron Core Copper Clad Alloy
- Arlon R38095R011 0.011" (0.279 mm) Partially Cross Linked Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved