BASF Ultramid® KR 4365 G5 BK 00100 35% Glass Filled PA6/6T FR (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® KR 4365 G5 BK 00100 35% Glass Filled PA6/6T FR (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resistant to electrolytic corrosion, resistant to soldering temperatures, can be electroplated.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Water Absorption 5.0 - 6.0 %
5.0 - 6.0 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.1 - 1.5 %
1.1 - 1.5 %
23°C; 50% RH; ISO 62
Viscosity Measurement 130
130
ISO 307
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
restricted
Linear Mold Shrinkage, Flow 0.0041 cm/cm
0.0041 in/in
TM=320°C, TW=100°C
0.0050 cm/cm
0.0050 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 140 MPa
20300 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 8.00 GPa
1160 ksi
ISO 527-1/-2
Tensile Creep Modulus, 1000 hours 6400 MPa

@Strain <=0.500 %
928000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 295 °C
563 °F
DIN 53765
Maximum Service Temperature, Air 125 °C
257 °F
for 50% loss of tensile strength after 20000hr
150 °C
302 °F
for 50% loss of tensile strength after 5000hr
270 °C
518 °F
Decomposition Temperature >= 350 °C
>= 662 °F
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 300 °C
572 °F
Feed Zone
Zone 2 310 °C
590 °F
Compression
Zone 3 320 °C
608 °F
Metering-zone
Zone 4 320 °C
608 °F
Nozzle
Melt Temperature >= 320 °C
>= 608 °F
Optimal
310 - 330 °C
590 - 626 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Injection-molding
100 °C
212 °F
Optimal
Drying Temperature 110 °C
230 °F
Dry Time 8 hour
8 hour
Descriptive Properties Value Comments
Color BK 00100
Commercial Status Europe
Ignition Temperature >470°C
ASTM D1929
Peripheral screw speed < 0.3 m/s