SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Styrene-Butadiene |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 33 g/10 min @Load 5.00 kg, Temperature 280 °C |
33 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | 10S reading; ASTM D2240 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 |
| 90 % | 90 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 20 % | 20 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 0.690 GPa | 100 ksi | 1 mm/min; ISO 527 |
| 0.840 GPa | 122 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 0.720 GPa | 104 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.790 GPa | 115 ksi | ISO 178 | |
| Izod Impact, Notched | 5.60 J/cm | 10.5 ft-lb/in | ASTM D256 |
| 1.70 J/cm @Temperature -30.0 °C |
3.18 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.47 @Frequency 1.00e+9 Hz |
2.47 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.0032 @Frequency 1.00e+9 Hz |
0.0032 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W84598L Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil LD 641.LN Molding, Extrusion and Compounding Resin (discontinued **)
- Taiwan Sheen Soon Sheenthane® A9080 Thermoplastic Polyurethane Elastomer
- Techmer ES HiFill® PBT 613
- ExxonMobil Santoprene® 201-55 Thermoplastic Elastomer
- Akzo Nobel Trigonox® K-90 Polymerization Initiator
- 3M Scotch-Weld™ DP608 Structural Adhesive
- Adell RR-14 Copolymer Polypropylene, 20% Glass Reinforced
- BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved