BASF Ultramid® FRee A3U40G5 25% Glass Filled PA66 FR (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® FRee A3U40G5 25% Glass Filled PA66 FR (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Flame retardant without halogens and red phosphorus, 25% glass fiber reinforced injection-molding grade; light colorable; outstanding mechanical and electrical properties.Information provided by BASF
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 4.0 - 4.6 %
4.0 - 4.6 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.1 - 1.5 %
1.1 - 1.5 %
23°C; 50% RH; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
restricted
Melt Flow 42.6 g/10 min

@Load 5.00 kg,
Temperature 275 °C
42.6 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 100 MPa
14500 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 2.8 %
2.8 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 10.0 GPa
1450 ksi
ISO 527-1/-2
Flexural Strength 220 MPa
31900 psi
at max force; ISO 178
Flexural Modulus 9.80 GPa
1420 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.0 - 23.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
11.7 - 12.8 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 70.0 - 100 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 - 55.6 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Melting Point 260 °C
500 °F
DIN 53765
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness >=0.400 mm
V-2

@Thickness >=0.0157 in
5VA

@Thickness >=1.60 mm
5VA

@Thickness >=0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00 Hz
3.8

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.017

@Frequency 1.00e+6 Hz
0.017

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe