BASF Ultramid® BG50XFI PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® BG50XFI PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid BG50XFI is an impact modified, injection molding type 6 nylon graft copolymer with superior impact resistance and flow especially for thinner walled parts and long flow lengths. It is also available in natural and pigmented versions. Copolymerization results in varying levels of toughness and flexibility combined with excellent thermal and chemical properties. Exhibits higher impact performance than that of conventional nylon homopolymers while maintaining good strength, chemical resistance and stiffness.Applications: Cellular phone housings, handheld device, caps, furniture rails, covers, mower decks and tool.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ASTM D792
Moisture Absorption at Equilibrium	2.4 %	2.4 %	50% RH; ASTM D570
	8.6 %	8.6 %	Saturation; ASTM D570

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa	10200 psi	ASTM D638
Elongation at Break	70 %	70 %	ASTM D638
Elongation at Yield	4.0 %	4.0 %	ASTM D638
Flexural Strength	95.0 MPa	13800 psi	ASTM D790
Flexural Modulus	2.39 GPa	347 ksi	ASTM D790
Izod Impact, Notched (ISO)	180 kJ/m²	85.7 ft-lb/in²	ISO 179
Dart Drop, Total Energy	201 J	148 ft-lb	BASF

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ASTM D648
UL RTI, Electrical	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	746B
UL RTI, Mechanical with Impact	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	746B
UL RTI, Mechanical without Impact	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	746B
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English
Melt Temperature	240 - 285 °C	464 - 545 °F
Mold Temperature	65.0 - 80.0 °C	149 - 176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Commercial Status	North America