Oxford Polymers 40GF 40% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 40% Glass Fiber |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers 40GF 40% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass Fiber Filled Polyetherimide for Extrusion and Injection MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Water Absorption | 0.13 % | 0.13 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 179 MPa | 26000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1500 ksi | ASTM D638 |
| Flexural Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 382 °C | 720 °F |
Users viewing this material also viewed the following:
- Ritelok PS65 General Purpose Pipe Sealant
- Mallard Creek Polymers Tykote® 6152 Styrene-Acrylic Emulsion
- SABIC Innovative Plastics ULTEM 2210F PEI
- Plastics Group Polifil® C-10 10% Calcium Carbonate-Reinforced Polypropylene
- Bond Laminates TEPEX® dynalite 102-RGUD600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate
- ATI Allegheny Ludlum Stainless Steel Type 201L, 50% Cold Work (UNS S20103)
- Loctite® 3883 Stencil Print Isotropic Epoxy Adhesive
- BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Dry)
- Schmolz + Bickenbach UGILEAN UGI 4116N Low Nickel Bar
Copyright © lookpolymers.com All Rights Reserved