Techmer ES HiFill FR® PBT 0166 B FR
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Techmer ES |
| Trade Name | HiFill FR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill FR® PBT 0166 B FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: Flame RetardantInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Break | 18 % | 18 % | ASTM D638 |
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | UL 746 |
Users viewing this material also viewed the following:
- RheTech Products T40P105-01 40% Talc Reinforced Polypropylene, Black
- Solvay TECHNYL® C 548B V15 Black PA6, 15% glass filled, DRY
- SABIC Innovative Plastics LNP Thermocomp DF0066P PC
- DuPont™ Bynel® 22E757 Modified Ethylene Acrylate
- DuPont™ Entira® AS MK 400 Ionomer Resin
- EMS-Grivory Grivory® XE 4106 black 9992 PA612-GF30
- DuPont Teijin Films Melinex® 1311 Polyester Film
- Aclo Accutech Polypropylene Homopolymer HP0339G20M10CL Glass/Mineral Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved