BASF Ultramid® B3WG7 BK 00564 30% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG7 BK 00564 30% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption 5.9 - 6.5 %
5.9 - 6.5 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.8 - 2.2 %
1.8 - 2.2 %
23°C; 50% RH; ISO 62
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
restricted
Melt Flow 66.45 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 66.45 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 105 MPa
15200 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 11.0 GPa
1600 ksi
ISO 527-1/-2
Flexural Strength 280 MPa
40600 psi
at max force; ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Izod Impact, Notched (ISO) 19.0 kJ/m²

@Temperature 23.0 °C
 9.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.80 J/cm²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 - 20.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 8.33 - 11.1 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 33.3 - 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
Specific Heat Capacity 1.40 J/g-°C
0.335 BTU/lb-°F
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20000hr
175 °C
347 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.9

@Frequency 1.00 Hz
 3.9

@Frequency 1.00 Hz
 IEC 60250
Dissipation Factor 0.021

@Frequency 1.00e+6 Hz
 0.021

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 450 V
450 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Color BK 00564
Commercial Status Europe