Solvay Specialty Polymers Amodel® A-4160 HSL Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-4160 HSL Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel A-4160 HSL resin is a 60% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits high modulus at elevated temperatures, a high heat deflection temperature and exceptional creep resistance. This material was designed for metal replacement applications. Its rapid crystallization and good flow characteristics allow shorter cycles for enhanced molding productivity. - Black: A-4160 HSL BK324Injection Notes: Injection Pressure: 3 to 4 in/secInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ISO 1183/A
Filler Content 60 %
60 %
Glass Fiber Reinforcement
Water Absorption 0.19 %

@Temperature 23.0 °C,
Time 86400 sec
0.19 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 79.6 MPa

@Temperature 200 °C
11500 psi

@Temperature 392 °F
ISO 527-2
244 MPa

@Temperature 23.0 °C
35400 psi

@Temperature 73.4 °F
ISO 527-2
Elongation at Break 1.4 %

@Temperature 23.0 °C
1.4 %

@Temperature 73.4 °F
ISO 527-2
3.3 %

@Temperature 200 °C
3.3 %

@Temperature 392 °F
ISO 527-2
Tensile Modulus 8.77 GPa

@Temperature 200 °C
1270 ksi

@Temperature 392 °F
ISO 527-2
23.3 GPa

@Temperature 23.0 °C
3380 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 137 MPa

@Temperature 200 °C
19900 psi

@Temperature 392 °F
ISO 178
385 MPa

@Temperature 23.0 °C
55800 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 8.50 GPa

@Temperature 200 °C
1230 ksi

@Temperature 392 °F
ISO 178
19.3 GPa

@Temperature 23.0 °C
2800 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact Unnotched 13.0 J/cm²
61.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 304 °C
579 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 318 - 324 °C
604 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 329 - 343 °C
624 - 649 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Additive Heat Stabilizer
Lubricant
Mold Release
Appearance Black
Automotive Specifications ASTM D6779 PA102G60
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Fast Molding Cycle
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Toughness
Heat Stabilized
High Heat Resistance
High Strength
Hot Water Moldability
Low CLTE
Lubricated
Ultra High Stiffness
Forms Pellets
Generic PPA
Processing Method Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Electronics
Automotive Under the Hood
Camera Applications
Cell Phones
Connectors
Electrical/Electronic Applications
Housings
Industrial Applications
Machine/Mechanical Parts
Metal Replacement
Transmission Applications