BASF Ultramid® 1000-11 NF2001 PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1000-11 NF2001 PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1000-11 NF2001 is a general purpose nylon 6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 % | 8.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | 50mm/min; ISO 527 |
| 83.0 MPa | 12000 psi | 2 in/min; ASTM Test | |
| Elongation at Break | 25 % | 25 % | 50mm/min, Nominal strain; ISO 527 |
| 60 % | 60 % | 2 in/min; ASTM Test | |
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM Test |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO Data |
| 2.90 GPa | 421 ksi | ASTM Test | |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm |
0.993 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 5.20 kJ/m² | 2.47 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.570 J/cm² | 2.71 ft-lb/in² | ISO 179 |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| 243 °C | 469 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75 |
| 77.0 °C | 171 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Radici Radilon® SERV3808 K (dry) Nylon 6
- LG Chemical Lupox® PBT-GP-2306FA 30% GFR Flame Retardant, UV Stabilized PBT
- Schott KG4 Short Pass Filter
- Shin-Etsu Silicones LIMSâ„¢ KE2090-60AB Elastomer
- Samyang Trirex® 3000H Polycarbonate, Low-temperature Impact
- Asahi Kasei Tenac®-C CF454 Copolymer Acetal Resin
- Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Moisture)
- Henkel Parcolac 2945 Sealer
- DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved