BASF Ultraform® N2200 G43 POM
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® N2200 G43 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a POM, injection-molding grade for parts requiring high stiffness and strength together with good mold release.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % | 0.90 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | ISO 2577 |
| Melt Flow | 6.622 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.622 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 164 MPa @Load 36.5 kg, Time 30.0 sec |
23800 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-2 |
| Modulus of Elasticity | 7.30 GPa | 1060 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.650 J/cm² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 4500 MPa | 653000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 170 °C | 338 °F | DIN 53765 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | ISO 75-2 |
| Vicat Softening Point | 160 °C | 320 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 |
| 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| 600 V | 600 V | Test solution B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | Hopper Throat |
| Zone 1 | 205 °C | 401 °F | Feed zone |
| Zone 2 | 205 °C | 401 °F | Compression |
| Zone 3 | 210 °C | 410 °F | Metering-zone |
| Zone 4 | 210 °C | 410 °F | Nozzle |
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection-molding |
| 210 °C | 410 °F | Optimal | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding |
| 100 °C | 212 °F | Optimal | |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 3 hour | 3 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Peripheral screw speed | <0.3 m/s | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs NI1000 NiSO4·7H2O Nickel sulfate heptahydrate
- Ravago Manufacturing Americas Hylon® N2040MHL Nylon 6 (Cond)
- ICO Polymers ICORENEâ„¢ 195-1325 LMDPE Rotational Molding Resin
- SABIC Innovative Plastics NORYL N190X PPE+HIPS (Asia Pacific)
- EMS-Griltech Grilon® XC 145 Nylon 6 Monofilament (Non-Set)
- Aclo Accucomp Polypropylene CPO402V Automotive Approved Copolymer Extrusion Grade
- Ascend Performance Materials Vydyne® R525H BK0201 Nylon 66, 25% Glass Reinforced, Conditioned
- PPT BP18 NiZn Ferrite Powder
- SABIC Innovative Plastics Lexan® FXG154 PC (Asia Pacific)
- Formosa Plastics Formolene® 4111T Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved