BASF Ultradur B 4406 G6 BKQ113 7110 30% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur B |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur B 4406 G6 BKQ113 7110 30% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur B 4406 G6 BKQ113 7110 is an UL V0 injection molding, pigmented black, PBT grade with 30% glass fiber reinforcement.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 105 cm³/g | 105 cm³/g | Viscosity number |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 154 MPa | 22300 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 143 MPa | 20700 psi | 5mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5mm/min; ISO 527 |
| 2.0 % | 2.0 % | ||
| Tensile Modulus | 11.7 GPa | 1700 ksi | 1mm/min; ISO 527 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| 223 °C | 433 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK7110 | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Flame retarding agent | |
| Heat stabilized or stable to heat | ||
| Light stabilized or stable to light | ||
| Lubricant | ||
| U.V. stabilized or stable to weather |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ ATH-000/02T Homopolymer - 2% PTFE (discontinued **)
- Abatron AboCast 8-24/Abocure 8-24 Epoxy (discontinued **)
- Saint-Gobain CHR® SG13-10(R) High Performance Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA
- Unipetrol PE HD LITEN® MB 68 HDPE
- Weartech International WT-700 Nickel Hardfacing & Wear Resistant Alloy
- BCC Products METAL-KAST/SLO BC 8010-2 Urethane Casting
- Arkema Group BONDINE® HX 8290 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved