- Acrylonitrile Butadiene Styrene (ABS), Molded
- Cossa Polimeri ESTADIENE 3015 MT Acrylonitrile Butadiene Styrene
Cossa Polimeri ESTADIENE 3015 MT Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTADIENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTADIENE 3015 MT Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABSMedium thermal resistance, high impact resistance at low temperature, good melt flow rate, high gloss, excellent processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D 638 |
| Elongation at Break | 15 % | 15 % | ASTM D 638 |
| Flexural Modulus | 2.15 GPa | 312 ksi | ASTM D 790 |
| Izod Impact, Notched | 3.00 J/cm @Temperature 0.000 °C |
5.62 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 3.50 J/cm @Temperature 23.0 °C |
6.56 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 102 °C @Load 5.00 kg |
216 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 110 °C @Load 0.999 kg |
230 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Resinoid 2225 Phenolic Molding, Cellulose Reinforced
- Momentive Performance Materials TSE3940 Gray Adhesive Sealant, Fast Cure Paste
- Teknor Apex APEX® 3211-90 Polyvinyl Chloride, Flexible
- Wieland 1941 Wilaform Platinum
- Arkema Group OREVAC® 9318 EVA Terpolymer
- Alliance Polymers Viprene™ G45A-32U-NAT Thermoplastic Vulcanizate Elastomer
- Bhansali Engineering Abstron KU660 ABS Heat Resistant
- DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved