BASF Novolen® 1040 RC Polypropylene, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 1040 RC Polypropylene, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection moldingsData was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 31 g/10 min @Load 2.16 kg, Temperature 230 °C |
31 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Break | 20 % | 20 % | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| Tensile Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | |
| 0.150 J/cm² @Temperature -30.0 °C |
0.714 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 135 µm/m-°C @Temperature 20.0 °C |
75.0 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | |
| Vicat Softening Point | 100 °C | 212 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.3 @Frequency 100 Hz |
2.3 @Frequency 100 Hz |
|
| 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.000070 @Frequency 100 Hz |
0.000070 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2204-25 CR-SX Fiberglass Reinforced SMC
- Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) (Unverified Data**)
- PolyOne Edgetek® SF-30CF/000 Polyphenylene Sulfide (PPS), Carbon Fiber Reinforced (discontinued **)
- Spartech Royalite R84 Proprietary Polymer Weather Resistant Sheet
- Techmer ES HiFill® PA6/6 GF43 L BKN001 43% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP RF00C PA 66 (Europe-Africa-Middle East)
- EMS-Grivory Grivory® F 47 NL nat 6028 PA6
- Bulk Molding Compounds BMC 620 Mineral Filled, Glass Fiber Reinforced Polyester Compound
- DuPont Teijin Films Mylar® MDA Polyester Film, 200 Gauge
Copyright © lookpolymers.com All Rights Reserved