Azoty Tarnow™ TARNOFORM 300 M POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	Azoty Tarnow™ (Zaklady Azotowe)
Trade Name	TARNOFORM
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azoty Tarnow™ TARNOFORM 300 M POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Tribological modified grade with addition of molybdenum disulphide, which causes decreased coefficient of friction and wear, especially for applications requiring high load at low sliding speed.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/in³	ISO 1183
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 190 °C	9.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	116	116	ISO 2039-2
Ball Indentation Hardness	143 MPa	20700 psi	358 N; ISO 2039-1
Tensile Strength, Yield	63.0 MPa	9140 psi	ISO 527
Elongation at Break	25 %	25 %	ISO 527
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Izod Impact, Notched (ISO)	5.60 kJ/m²	2.67 ft-lb/in²	1A; ISO 180
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	1eA; ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	167 °C	333 °F	10°C/min.; ISO 3146
Maximum Service Temperature, Air	100 °C	212 °F
Deflection Temperature at 1.8 MPa (264 psi)	115 °C	239 °F	ISO 75
Vicat Softening Point	156 °C	313 °F	50 N; ISO 306
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	4.1 @Frequency 1e+6 Hz	4.1 @Frequency 1e+6 Hz	IEC 60250
Dielectric Strength	25.0 kV/mm	635 kV/in	IEC 60243
Dissipation Factor	0.0105 @Frequency 1e+6 Hz	0.0105 @Frequency 1e+6 Hz	IEC 60250
Arc Resistance	1.9 sec	1.9 sec
Comparative Tracking Index	600 V	600 V	IEC 112

Processing Properties	Metric	English	Comments
Processing Temperature	180 - 230 °C	356 - 446 °F	Barrel temperature
Mold Temperature	60.0 - 120 °C	140 - 248 °F