Azoty Tarnow™ TARNOFORM 300 HI2 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 HI2 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rubber modified grade with very high impact strength and damping capacity.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0265 cm/cm @Thickness 4.00 mm |
0.0265 in/in @Thickness 0.157 in |
|
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ISO 2039-2 |
| Ball Indentation Hardness | 97.0 MPa | 14100 psi | 358 N; ISO 2039-1 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
| Elongation at Break | 58 % | 58 % | ISO 527 |
| Flexural Strength | 46.0 MPa | 6670 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.24 ft-lb/in² | 1A; ISO 180 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.48 J/g-°C | 0.354 BTU/lb-°F | |
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75 |
| Vicat Softening Point | 137 °C | 279 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
IEC 60250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243 |
| Dissipation Factor | 0.0255 @Frequency 1e+6 Hz |
0.0255 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 210 °C | 356 - 410 °F | Barrel temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8981X (899XP-1) (UF) Synthetic Oil
- Pyrotek TS-207 Thermoset Electrical Insulation Product
- Pinnacle Polymers 5135 C Clarified Polypropylene Random Copolymer, Injection Molding Grade
- Lanxess Pocan® KU 2-7205 000000 PBT
- Techmer ES HiFill® PA6/6 GF30 HS L 30% Glass Filled
- SABIC Innovative Plastics NORYL NH5020 PPE+PS (Europe-Africa-Middle East)
- Loctite® 272 High Temperature/High Strength Threadlocker
- Chi Mei Kibilac® PW-978B ASA, High Heat
- DuPont Performance Polymers Zytel® HTN 53G60LRHF BK083 Polyphthalamide (PPA) (Unverified Data**)
- Chosun Refractories CTC-85TD Monolithic Refractories for Ladle and Tundish
Copyright © lookpolymers.com All Rights Reserved