IRPC Polimaxx Porene KU900 Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Porene |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | IRPC Polimaxx Porene KU900 Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications:extrusion sheetrefrigerator door liners and inner box linerspicnic coolerssnow boatsluggage cases
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.0 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C |
7.0 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 <br>@Thickness 6.35 mm,<br> Temperature 23.0 °C |
105 <br>@Thickness 0.250 in,<br> Temperature 73.4 °F |
ASTM D785 |
| Tensile Strength, Ultimate | 43.1 MPa <br>@Temperature 23.0 °C |
6260 psi <br>@Temperature 73.4 °F |
ASTM D638 |
| Flexural Yield Strength | 59.3 MPa <br>@Temperature 23.0 °C |
8610 psi <br>@Temperature 73.4 °F |
ASTM D790 |
| Flexural Modulus | 2.01 GPa <br>@Temperature 23.0 °C |
292 ksi <br>@Temperature 73.4 °F |
ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm <br>@Thickness 6.35 mm,<br> Temperature 23.0 °C |
5.51 ft-lb/in <br>@Thickness 0.250 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C <br>@Thickness 6.35 mm |
198 °F <br>@Thickness 0.250 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C <br>@Thickness 6.35 mm |
185 °F <br>@Thickness 0.250 in |
ASTM D648 |
| Flammability, UL94 | HB <br>@Thickness 1.50 mm |
HB <br>@Thickness 0.0591 in |
|
| HB <br>@Thickness 3.00 mm |
HB <br>@Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 240 °C | 356 - 464 °F | |
| Drying Temperature | 80.0 - 90.0 °C <br>@Time 7200 - 18000 sec |
176 - 194 °F <br>@Time 2.00 - 5.00 hour |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-86 Clear General Purpose Acrylic Resin
- Nylene® PA6 Impact Modified 323 HS Nylon 6
- Polymax® Maxelast® P1755 TPE, PP Overmold or Standalone use
- Premix Thermoplastics PRE-ELEC® PPE 1462 (discontinued **)
- Materion Brush 1915â„¢ Annealed Temper Wire
- ExxonMobil 2 Mobilith AW Series
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with No Plasticizer
- A. Schulman PP 828-01 Polypropylene Molding Grade Impact Polypropylene
- Carmel Olefins CAPILENE® SW 75 AV Polypropylene Impact Copolymer
- Braskem RP 144 Coating Polypropylene
Copyright © lookpolymers.com All Rights Reserved