Azoty Tarnow™ TARNOFORM 300 GB6 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 GB6 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass beads filled grade with increased stiffness and hardness with lowered shrinkageInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | ISO 62 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ISO 2039-2 |
| Ball Indentation Hardness | 183 MPa | 26500 psi | 358 N; ISO 2039-1 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ISO 75 |
| Vicat Softening Point | 156 °C | 313 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.4 @Frequency 1e+6 Hz |
4.4 @Frequency 1e+6 Hz |
IEC 60250 |
| 4.9 @Frequency 100 Hz |
4.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.0115 @Frequency 1e+6 Hz |
0.0115 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | Barrel temperature |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
Users viewing this material also viewed the following:
- Hong Kun Group AO B1171 Antioxidant
- Menzolit Menzolit® HPC 1200 Unsaturated Polyester UP
- SABIC Innovative Plastics Valox® AB9515 ABS+PBT (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP RW004 PA 66 (Asia Pacific)
- NAPCO C95 Magnesite
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
- Aclo Accutech Polypropylene Homopolymer HP0334M40CL Mica Reinforced Coupled
- 3A Composites Core Materials AIREX® T90.150 Easy Processing Structural FST Foam
- MetalTek MTEK H13 UNS T90813 Tool Steel
- ATI Wah Chang Zirconium Oxynitrate, ZrO(NO3)2-2H2O
Copyright © lookpolymers.com All Rights Reserved