Azoty Tarnow™ TARNOFORM 300 GB2 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 GB2 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% glass beads filled grade with increased stiffness and hardness with lowered shrinkageInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | ISO 62 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ISO 2039-2 |
| Ball Indentation Hardness | 182 MPa | 26400 psi | 358 N; ISO 2039-1 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Break | 12 % | 12 % | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 1A; ISO 180 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ISO 75 |
| Vicat Softening Point | 155 °C | 311 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 60250 |
| 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Dissipation Factor | 0.0095 @Frequency 1e+6 Hz |
0.0095 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | Barrel temperature |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F |
Users viewing this material also viewed the following:
- MV Labs ZN100 Zn(OAC)2·xH2O Zinc acetate hydrate
- SABIC Innovative Plastics Cycoloy® CX7110 PC+ABS
- Polykemi AB SCANMID 6 B12^ F30 AS Nylon 6, Glass Fiber Reinforced
- Solvay Specialty Polymers Tecnoflon® PL 458 Fluoroelastomer
- Techmer ES Plastiblend® ABS 8007
- Chase Plastics CP Pryme® N310L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated, Recycled Content
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-330 (HAF)
- Dow VORANOL™ 4815 Polyether Polyol
- 3M Scotch® 2480S Ultimate Paint Edge Masking Tape
- Axiall 8266 Rigid PVC, Extrusion, Natural
Copyright © lookpolymers.com All Rights Reserved