Asia International Enterprise (Hong Kong) 60G8 Nylon 66, 40% Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 60G8 Nylon 66, 40% Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc @Temperature 23.0 °C |
1.50 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 216 MPa | 31300 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 299 MPa | 43400 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 12.3 GPa | 1780 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
2.39 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- H.C. Starck Amperit® 716.066 Chromium Oxide-Titanium Oxide-Silicon Oxide 92-3-5 (Cr2O3-TiO2-SiO2)
- Multibase Multi-Flex® A 7041 Clear TPE Thermoplastic Elastomer
- Sekisui PIOCELAN OP-15ENS (Antistatic) Moldable Polymer Foam
- Silberline "A" Series A-226
- Unitika A1030FR PA6, Conditioned
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- Ensinger Hydel® PC-7 Polycarbonate (PC)
- DuPont Performance Polymers Zytel® LC6210 BK010 Nylon 612 (Unverified Data**)
- Ashley Polymers Ashlene® P266 PPO, 30% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved