E-Polymers SEPAZ® LB60 PA6 LFT Resin

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	E-Polymers Co. Ltd.
Trade Name	SEPAZ®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers SEPAZ® LB60 PA6 LFT Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and delivers optimal reinforcement to the plastic matrix in contrast to conventional short glass fiber-reinforced thermoplastics. Molded parts made of SEPAZ LFT are used in virtually every sector of consumer and industrial manufacturing, including automotive, recreation & sports, marine, food & beverage.Information Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.71 g/cc	1.71 g/cc	ASTM D792
Water Absorption	0.70 % @Time 86400 sec	0.70 % @Time 24.0 hour
Linear Mold Shrinkage	0.0015 cm/cm	0.0015 in/in
Linear Mold Shrinkage, Transverse	0.0020 cm/cm	0.0020 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	235.44 MPa	34148 psi	ASTM D638
Elongation at Break	1.5 %	1.5 %	ASTM D638
Flexural Strength	353.16 MPa	51222 psi	ASTM D790
Flexural Modulus	14.715 GPa	2134.2 ksi	ASTM D790
Izod Impact, Notched	3.43 J/cm @Temperature 23.0 °C	6.43 ft-lb/in @Temperature 73.4 °F	ASTM D256
	3.43 J/cm @Temperature -30.0 °C	6.43 ft-lb/in @Temperature -22.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	215 °C	419 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	90.0 - 120 °C	194 - 248 °F