Ashley Polymers Ashlene® 180 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 180 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A general purpose, high viscosity, natural.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
| Elongation at Break | 65 % | 65 % | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Shear Strength | 55.0 MPa | 7980 psi | ASTM D732 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-1000 IG UC Clear High Impact Acrylic Resin
- Mitsubishi Hostaphan® RN, 15 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1000 PC (Asia Pacific)
- Samsung Cheil Industries Infino® LS-1150G PC/ABS, 15% Glass Filled FR
- A. Schulman INVISION™ VX-5090UI Soft Touch Polyolefin Thermoplastic
- A. Schulman POLYBATCH™ White LL8425 AP Concentrate Based In LLDPE
- Fainplast Compounds HL 94 Flexible PVC, Insulation for High Temperatures
- BASF Elastollan R 1001 10% Glass Filled TPUR
- Sinotek Materials MD-6 Graphite Emulsion
- Materion ToughMet® T3 CX105 (OD
Copyright © lookpolymers.com All Rights Reserved