Ascend Performance Materials Vydyne® 67R Nylon 66, Heat Stabilized, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® 67R Nylon 66, Heat Stabilized, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® 67R is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 67R resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.Availability:Asia PacificEuropeNorth America Additives: Heat Stabilizer Features: Gasoline ResistanceGeneral Purpose Good Chemical ResistanceGood ToughnessHeat StabilizedHigh Melt StabilityHigh RigidityHigh StrengthHigh ViscosityOil ResistantSolvent ResistantUses:Automotive ApplicationsFilmIndustrial ApplicationsMonofilamentsProfilesRodsSheetTubing Appearance: Natural ColorForms: PelletsProcessing Method: ExtrusionInformation provided by Ascend Performance Materials.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Water Absorption	8.5 % @Time 86400 sec	8.5 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.5 %	2.5 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.022 cm/cm @Diameter 2.00 mm	0.022 in/in @Diameter 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.021 cm/cm @Diameter 2.00 mm	0.021 in/in @Diameter 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	70.0 MPa	10200 psi	ISO 527-2
Tensile Strength, Yield	55.0 MPa	7980 psi	ISO 527-2
Elongation at Break	250 %	250 %	ISO 527-2
Elongation at Yield	20 %	20 %	ISO 527-2
Tensile Modulus	1.90 GPa	276 ksi	ISO 527-2
Flexural Strength	20.0 MPa	2900 psi	ISO 178
Flexural Modulus	0.750 GPa	109 ksi	ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 180
	30.0 kJ/m² @Temperature 23.0 °C	14.3 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	3.00 J/cm² @Temperature 23.0 °C	14.3 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA