PolyOne Geon™ Vinyl Dry Blend E7000 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Dry Blend E7000 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
60 degree gloss comparisons: Geon E7000 is 47-49;Geon E7456 is 40-49;Geon E7130 is 38-43;Geon E7370 is 26-31Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | ASTM D2240 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.65 GPa | 384 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
| Flexural Modulus | 2.78 GPa | 403 ksi | ASTM D790 |
| Izod Impact, Notched | 1.80 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
3.37 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| Dart Drop Total Energy | 66.7 J/cm @Temperature 23.0 °C |
0.125 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 178 J/cm @Temperature 23.0 °C |
0.333 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C | 35.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.9 °C @Thickness 3.18 mm |
174 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 81.1 °C @Thickness 3.18 mm |
178 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 77.8 °C @Thickness 3.18 mm |
172 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 204 °C | 379 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | High Impact Resistance | |
| Forms | Powder | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| Profile Extrusion | ||
| PVC Cell Classification | 1-32443-43-0000 | ASTM D4216 |
| 13344 | ASTM D1784 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Outdoor Applications |
Users viewing this material also viewed the following:
- Nye Lubricants 271 (SO) Synthetic Oil
- Momentive Performance Materials Silplusâ„¢ 70 MP Heat Cured Rubber
- KaMin Polyfil® WC-426 Kaolin Clay - Calcined
- A. Schulman POLYBATCH™ Blue 40567 Concentrate Based In LDPE
- ExxonMobil Enable™ 23-05NA Metallocene Polyethylene Resin
- 3M 3369 General Purpose Aluminum Foil Tape
- A. Schulman ComAlloy Hiloy® 415 Polyester - PBT, Glass Reinforced
- PolyOne Edgetek® UR-20GF/000 Natural Thermoplastic Polyurethane (Ether-Based), 20% Glass Fiber Reinforced (di
- Schmolz + Bickenbach Cryodur® 2990 Cold Work Die Steel
Copyright © lookpolymers.com All Rights Reserved