Ascend Performance Materials Vydyne® 66Z Nylon 66, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 66Z Nylon 66, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 66Z is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66Z resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.Availability:Asia PacificEuropeNorth America Features: Gasoline ResistanceGeneral Purpose Good Chemical ResistanceGood Melt StrengthGood ToughnessHigh RigidityHigh StrengthHigh ViscosityOil ResistantSolvent ResistantUses:Cast FilmFilmFood PackagingIndustrial ApplicationsMonofilamentsRodsSheetTubing Appearance: Natural ColorForms: PelletsProcessing Method: Extrusion and Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 8.5 %

@Time 86400 sec
8.5 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.022 cm/cm

@Diameter 2.00 mm
0.022 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.021 cm/cm

@Diameter 2.00 mm
0.021 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
ISO 527-2
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527-2
Elongation at Break 250 %
250 %
ISO 527-2
Elongation at Yield 20 %
20 %
ISO 527-2
Tensile Modulus 1.90 GPa
276 ksi
ISO 527-2
Flexural Strength 20.0 MPa
2900 psi
ISO 178
Flexural Modulus 0.750 GPa
109 ksi
ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180
30.0 kJ/m²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA