SABIC Innovative Plastics Valox® V9280LW PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V9280LW PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glassfiber / Mineral Filled PET, Impact Modifier, Mold Release, Heat StabilizedThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % @Temperature 23.0 °C |
0.25 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.5 GPa | 1810 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 235 °C | 455 °F | Rate B/50; ISO 306 |
| 240 °C | 464 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- MV Labs PD480 [Pd(NH3)]4Cl2·H2O Tetraminepalladium(II) chloride monohydrate
- Polykemi AB POLYfill PPC T1035 Polypropylene Copolymer, Mineral Reinforced
- Polimeri Europa SINKRAL PD H330/S ABS, Heat Stabilized (discontinued **)
- Solvay Specialty Polymers Solef® 31008 PVDF Copolymer (discontinued **)
- Rostone Rosite® C200BS ESD SMC, Conductive Thermoset Polyester, 10% Glass Reinforced (discontinued **)
- NAPCO White Fused Alumina
- Dow Corning XIAMETER® PMCPPMX-200 20Cs Silicone Fluid
- Elgiloy® Co-Cr-Ni Alloy, Strip, 40% Cold Reduction
- Fainplast Compounds Hax™ HFC 0108/4 Flame Retardant Polyolefin Cable Compound
- 3M Dyneon™ PVDF 6108/0001 Polyvinylidene Fluoride
Copyright © lookpolymers.com All Rights Reserved