DuPont Teijin Films Teonex® Q51 Polyester Film, 48 Gauge

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer	DuPont Teijin Films (DTF)
Trade Name	Teonex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Teijin Films Teonex® Q51 Polyester Film, 48 Gauge.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Teonex® Q51 is biaxially oriented polyethylene naphthalate (PEN) film. It is slightly hazy with excellent handling properties for general purpose. It is commercially available in nominal 48 - 1000 gauge. Approvals: UL 94 VTM-2 - 100 - 1000 gauge (0.025 - 0.25 mm) and UL Component Registration (RTI = 180/160°C) - Relative Thermal Index (RTI) = 180°C (Elect), 160°C (Mech)Also available in 1000 GaugeInformation provided by DuPont.

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	JIS C-2151
Moisture Absorption at Equilibrium	0.30 %	0.30 %	TDF Method
Water Vapor Transmission	104 g/m²/day	6.70 g/100 in²/day	JIS Z0208

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	90 %	90 %	JIS C-2318 (Modified to TDF)
Film Elongation at Break, TD	85 %	85 %	JIS C-2318 (Modified to TDF)
Coefficient of Friction, Dynamic	0.30	0.30	JIS C2151
Coefficient of Friction, Static	0.30	0.30	JIS C2151
Film Tensile Strength at Break, MD	276 MPa	40000 psi	JIS C-2318 (Modified to TDF)
Film Tensile Strength at Break, TD	262 MPa	38000 psi	JIS C-2318 (Modified to TDF)

Thermal Properties	Metric	English	Comments
Melting Point	269 °C	516 °F	DSC
Glass Transition Temp, Tg	121 °C	250 °F	DSC
UL RTI, Electrical	160 °C	320 °F
UL RTI, Mechanical without Impact	180 °C	356 °F
Shrinkage, MD	0.40 % @Temperature 150 °C	0.40 % @Temperature 302 °F	JIS C-2318 (Modified to TDF)
	2.0 % @Temperature 200 °C, Time 600 sec	2.0 % @Temperature 392 °F, Time 0.167 hour	Unrestrained
Shrinkage, TD	0.00 % @Temperature 150 °C	0.00 % @Temperature 302 °F	JIS C-2318 (Modified to TDF)
	1.0 % @Temperature 200 °C, Time 600 sec	1.0 % @Temperature 392 °F, Time 0.167 hour	Unrestrained

Optical Properties	Metric	English	Comments
Haze	14 %	14 %	JIS K6714
Transmission, Visible	82 %	82 %	JIS K6714
UV Transmittance	8.0 % @Wavelength 360 nm	8.0 % @Wavelength 360 nm	TDF Method

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+18 ohm-cm	1.00e+18 ohm-cm	JIS C-2318
Surface Resistivity per Square	2.00e+17 ohm	2.00e+17 ohm	JIS C-2151
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	JIS C-2318
	2.9 @Frequency 1.00e+9 Hz	2.9 @Frequency 1.00e+9 Hz	JIS C-2318
	3.0 @Frequency 60.0 Hz	3.0 @Frequency 60.0 Hz	JIS C-2318
Dielectric Strength	300 kV/mm	7620 kV/in	JIS C-2318
Dissipation Factor	0.0030 @Frequency 60.0 Hz, Temperature 25.0 °C	0.0030 @Frequency 60.0 Hz, Temperature 77.0 °F	JIS C-2318
	0.0050 @Frequency 1.00e+6 Hz, Temperature 25.0 °C	0.0050 @Frequency 1.00e+6 Hz, Temperature 77.0 °F	JIS C-2318
	0.0050 @Frequency 1.00e+9 Hz, Temperature 25.0 °C	0.0050 @Frequency 1.00e+9 Hz, Temperature 77.0 °F	JIS C-2318

Descriptive Properties	Value	Comments
Coefficient of Hygroscopic Expansion	0.000011/%RH	TDF Method
F5	19 kpsi	TD, TDF Method
	19 kpsi	MD, TDF Method
Surface Roughness	13/11 nm	TDF Method (Inside/Outside)
Tear Propagation	1.3 lb	MD, TDF Method
	1.3 lb	TD, TDF Method
Wettability (water angle)	70°	TDF Method