Aremco Aremco-Bond™ 2150 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2150 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ceramic-Filled, Fast-Setting, High Vibration Resistance and Bond Strength. Ideal for bonding ceramic wear tiles.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | |
| Flexural Strength | 81.4 MPa | 11800 psi | ASTM D790 |
| Shear Strength | 16.2 MPa | 2350 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 32.4 µm/m-°C @Temperature 20.0 °C |
18.0 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Shrinkage | 0.40 % | 0.40 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Dielectric Constant | 4.2 @Frequency 1000 Hz |
4.2 @Frequency 1000 Hz |
|
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | |
| Dissipation Factor | 0.030 | 0.030 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min @Temperature 23.9 °C |
1.00 hour @Temperature 75.0 °F |
+ 4 hr at 175°F, Alternate |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
Recommended | |
| Pot Life | >= 480 min @Temperature 25.0 °C |
>= 480 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Good | |
| Color | Light Gray | |
| Mix Ratio By Weight | 100:13 | resin:hardener |
| Viscosity | Paste |
Users viewing this material also viewed the following:
- Huntsman PE1903 EVA Film Extrusion (discontinued **)
- Lubriplate Vacuum Pump Oil Light Specialty Oil and Fluid
- Lehmann & Voss LUVOCOM® 1105-0950/RD PEEK, unreinforced
- Kinlead PT21 Adhesive Tape Grade BOPP Plain Film (thickness: 60 µm)
- Sharadaa Ceramics REFINSUL ZAP-019 Insulating Castables
- Unifrax Fiberfrax® HSA Ceramic Fiber Paper
- Zircar Refractory Composites RS-3000 ALUMINA FELT
- Arlon Thermabond®-II 99760N015 0.015" (0.381 mm) Unsupported/Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved