Asahi Kasei Xyron® 100Z Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® 100Z Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame RetardantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 59.0 MPa | 8560 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
2.75 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 1.96 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
3.67 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | 50% RH; ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | 50% RH; ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
3.0 mm 5VA; ASTM D150 |
| 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Dielectric Strength | 29.0 kV/mm @Thickness 2.00 mm |
737 kV/in @Thickness 0.0787 in |
Short time; ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 60 Hz |
0.0030 @Frequency 60 Hz |
50% RH; ASTM D150 |
| 0.0040 @Frequency 1e+6 Hz |
0.0040 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Arc Resistance | 80 sec | 80 sec | Tungsten; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 270 °C | 428 - 518 °F | Resin Temperature |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- Ovation Polymers OpteSTAT™ MB PC 1000 Polycarbonate-based Carbon Nanotube Compound
- DuPont Performance Polymers Crastin® 6134 NC010 PBT (Unverified Data**)
- LG Chemical LUMID GP2330BL PA66+GF33%, General Purpose
- Shakespeare WN-18 diameter 0.4 mm Nylon 6 Monofilament
- SABIC Innovative Plastics LNP THERMOCOMP DF00A8P PC (Asia Pacific)
- Borealis Borcoat™ EA165E Elastomer Modified Polypropylene for Extrusion
- Universal Wire Works ER321 Stainless Steel Bare Wire
- DuPont Performance Polymers Crastin® HR5315HFS NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- ExxonMobil LD 129.24 Cast Overwrap Film Resin
Copyright © lookpolymers.com All Rights Reserved