- Entec Hypro™ PPH-T30 Homopolymer Polypropylene, 30% Talc Reinforced
Entec Hypro™ PPH-T30 Homopolymer Polypropylene, 30% Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hypro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hypro™ PPH-T30 Homopolymer Polypropylene, 30% Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Entec
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Melt Flow | 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
10.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 14.0 % | 14.0 % | ASTM D638 |
| Elongation at Yield | 5.00 % | 5.00 % | ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 2.414 GPa | 350.1 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 HS-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced
- RheTech Products HP532-00 20% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Natural
- DSM Akulon® Ultraflow™ K-FKGS6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry) (discontinued **
- DuPont Vamac® G/HVG Sample Compound (discontinued **)
- Kotec Carbotex KG-30F15 Polycarbonate, Wear Resistant, 30% Glass Fiber Reinforced
- H.C. Starck Amperit® 703.1 Chromium Oxide (Cr2O3) 99.5%
- Sapco 99.9% Aluminum Oxide
- Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY
- Tra-Con Tra-Bond 526M02 High Tg Fiber Optic Adhesive
- Esstech X-738-0000 Ethoxylated Bis Phenol A Dimethacrylate, C83H144O34
Copyright © lookpolymers.com All Rights Reserved