- HOME
- POLYMER SEARCH
- Thermoplastic
- Acetal (POM)
- Acetal Copolymer, Unreinforced
- Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat (discontinued **)
Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Antistatic grade containing special carbon black.Applications: Parts requiring antistatic properties.This product is not a part of the standard product line dated 2003.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | Asahi Chemical test |
| Melt Flow | 10 g/10 min | 10 g/10 min | melt index; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 5 mm/min; parallel to flow; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; parallel to flow; ASTM D638 |
| Flexural Yield Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D790 |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 200 °C | 356 - 392 °F | Resin temp |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F |
Users viewing this material also viewed the following:
- Parker Chomerics SOFT-SHIELD® 3700 High Temperature Conductive Fabric Over Foam
- M. Holland Company SA311 Styrene Acrylonitrile
- Kennametal Stellite Stellite® 6 PM cast
- Kraton® G7705 GI-N (SEBS) Compound
- Momentive Performance Materials RTV60 Red Extreme High Temperature Potting/Encapsulating Compound
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Precipitated Calcium Carbonate
- EMS-Grivory Grivory® TSG-30/4 LF 15 PA666-(GF+Z)45
- California Fine Wire Stablohm 610 Nickel, Chromium and Iron Resistance Wire
- Loctite® FLASHCURE™ 4302 Light Cure Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved